GB/T 24234-2009铸铁光谱标样
标样编号 | HKK A01085 | HKK A01075 | BS LH01058 | BS LH01066 | BS LH01056 | BS LH01076 | BS SY01156 | HKK A01011 | HKK A01001 |
Al | 0.077 | 0.058 | 0.054 | 0.011 | 0.073 | 0.072 | 0.172 | 0.054 | 0.024 |
As | 0.022 | - | 0.0026 | 0.014 | - | - | 0.0053 | - | - |
B | 0.036 | 0.0036 | 0.014 | 0.049 | 0.013 | 0.055 | 0.072 | 0.0064 | 0.0014 |
Bi | 0.005 | -0.002 | - | - | - | - | - | -0.002 | -0.002 |
C | 2.82 | 3.15 | 2.13 | 3.01 | 4.07 | 2.25 | 4.03 | 2.75 | 3.98 |
Ca | - | - | - | - | - | - | - | - | - |
Ce | - | 0.027 | - | - | 0.0006 | 0.003 | - | 0.026 | 0.017 |
Co | 0.004 | 0.022 | 0.028 | 0.012 | 0.027 | 0.094 | 0.02 | 0.015 | 0.045 |
Cr | 0.64 | 0.037 | 0.615 | 0.276 | 2.12 | 0.493 | 0.058 | 0.239 | 0.032 |
Cu | 0.16 | 0.012 | 0.444 | 0.828 | 0.266 | 1.65 | 1.26 | 0.73 | 0.385 |
Fe | - | - | - | - | - | - | - | - | - |
La | - | - | - | - | 0.0003 | 0.001 | - | - | - |
Mg | - | 0.044 | - | - | 0.0024 | 0.0056 | - | 0.021 | -0.04 |
Mn | 0.996 | 0.718 | 1.67 | 0.681 | 0.22 | 1.17 | 0.103 | 0.71 | 1.322 |
Mo | 0.114 | 0.185 | 0.17 | 0.319 | 0.724 | 0.253 | 1.18 | 0.22 | 0.152 |
N | - | - | - | - | - | - | - | 0.0043 | 0.0045 |
Nb | - | - | 0.303 | 0.11 | 0.022 | 0.117 | 0.092 | 0.032 | 0.008 |
Ni | 0.174 | 0.367 | 0.082 | 0.592 | 1.46 | 0.623 | 1.2 | 0.389 | 0.411 |
P | 0.48 | 0.037 | 0.076 | 0.371 | 0.054 | 0.375 | 0.042 | 0.06 | 0.19 |
Pb | 0.007 | 0.007 | 0.0016 | 0.004 | - | - | 0.0004 | 0.01 | 0.014 |
S | 0.073 | 0.006 | 0.027 | 0.064 | 0.041 | 0.095 | 0.019 | 0.007 | 0.008 |
Sb | 0.046 | - | 0.105 | 0.065 | - | - | 0.198 | 0.019 | -0.004 |
Si | 2.57 | 2.72 | 3.69 | 1.98 | 1.48 | 2.66 | 0.57 | 3.1 | 1.63 |
Sn | 0.041 | 0.032 | 0.037 | 0.06 | 0.146 | 0.046 | 0.051 | 0.039 | 0.067 |
Ti | 0.085 | 0.046 | 0.097 | 0.111 | 0.042 | 0.184 | 0.057 | 0.13 | 0.065 |
V | 0.34 | 0.015 | 0.167 | 0.302 | 0.09 | 0.518 | 0.579 | 0.356 | 0.152 |
W | 0.011 | 0.021 | 0.021 | 0.437 | 0.039 | 0.434 | 0.103 | 0.079 | 0.038 |
Zn | -0.003 | 0.009 | - | - | - | - | - | 0.009 | 0.013 |
Zr | -0.002 | -0.007 | - | - | - | - | - | - | - |